Bulk-like behavior in the temperature driven martensitic transformation of Cu-Zn-Al thin films with 2H structure

Cargando...
Miniatura

Tipo de recurso

ARTÍCULO CIENTÍFICO

Responsable institucional (informe)

Compilador

Diseñador

Contacto (informe)

Promotor

Titular

Inventor

Tutor de tesis

Solicitante

Afiliación

Fil: Haberkorn, N. Comisión Nacional de Energía Atómica. Instituto Balseiro; Argentina; Universidad Nacional de Cuyo; Argentina
Fil: Condó, A.M. Comisión Nacional de Energía Atómica. Instituto Balseiro; Argentina; Universidad Nacional de Cuyo; Argentina
Fil: Espinoza, C. Comisión Nacional de Energía Atómica. Instituto Balseiro; Argentina; Universidad Nacional de Cuyo; Argentina
Fil: Jaureguizahar, S. Comisión Nacional de Energía Atómica. Instituto Balseiro; Argentina; Universidad Nacional de Cuyo; Argentina
Fil: Guimpel, J. Comisión Nacional de Energía Atómica. Instituto Balseiro; Argentina; Universidad Nacional de Cuyo; Argentina
Fil: Lovey, F.C. Comisión Nacional de Energía Atómica. Instituto Balseiro; Argentina; Universidad Nacional de Cuyo; Argentina

Sede CNEA

Centro Atómico Bariloche

Fecha de publicación

Fecha de creación

Idioma

eng

Nivel de accesibilidad

Proyectos de investigación

Unidades organizativas

Número de la revista

Resumen

This paper reports on the possibility to obtain Cu–Zn–Al films with 2H martensitic structure by fixing the valence electron concentration per atom (e/a) ≈1.53. Films with thickness of ≈5 μm with micrometric grains show martensitic transformation temperature and hysteresis values close to the ones found in bulk samples. This result is different to the one found in Cu–Zn–Al thin films with 18R martensitic structure and similar microstructure, in which the hysteresis presents an increment (≈10 times) compared to bulk samples. This difference can be associated to the intrinsic nature of the 2H transformation which requires more undercooling to produce the nucleation of the martensitic phase. The driving force for the burst-type martensitic transformation decreases the influence of the microstructure in the transformation.

Descripción

Palabras clave

Citación

Journal of Alloys and Compounds. Vol. 591, no. (2014), p. 263-267