Tensile behavior upon ordering of Ni3Fe single crystals.

Cargando...
Miniatura
Fecha
1967
Tipo de recurso
INFORME
Autor / Creador principal
Responsable institucional (informe)
Compilador
Diseñador
Contacto (informe)
Promotor
Productor
Titular
Inventor
Tutor de tesis
Solicitante
Afiliación
Fil: Victoria, M. Comisión Nacional de Energía Atómica; Argentina
Vidoz, A. E. Comisión Nacional de Energía Atómica; Argentina
Comisión Nacional de Energía Atómica; Argentina
Sede CNEA
Fecha de publicación
1967
Fecha de creación
Idioma
eng
Nivel de accesibilidad
Condiciones de uso
Versión
Versión publicada
Identificador CNEA
01.67.03
Identificador (documentos oficiales)
ISBN
ISSN
Cobertura espacial
Cobertura temporal
Materia INIS
Palabras clave
MONOCRYSTALS
TENSILE STRENGTH
HARDENING
STRAIN AGING
NICKEL
IRON
Macro-area temática
Formato (extensión)
53 p.
Editor
Comisión Nacional de Energía Atómica (Argentina)
Es parte de
Es parte la serie
Agrupamiento documental - Sección
Agrupamiento documental - Serie
Institución académica
Titulación
Fecha de resolución
Fecha de presentación de solicitud
Resolución
Estado
Prioridad - fecha
Estado de licenciamiento
Nº de prioridad
Nº de patente
Nº de solicitud
País de registro
Nivel de madurez de la tecnología
Campo de aplicación
Campo de desarrollo
Resumen
The tensile properties of ordered and disordered Ni3Fe single crystal have been investigated. Also, poly crystalline specimens have been tested to show the influence of grain size on the deformation characteristics of Ni3Fe. Measurements have been made to determine the influence of parameters such as the initial orientation of the tensile axis of single crystals, the ordered domain size, and the test temperature on the mechanical properties of Ni3Fe. Tensile axis reorientation during deformation was followed with x-ray techniques. It was found that in ordered single crystals, the measured tensile axis rotation agrees well with the calculated values if one activated glide system is assumed. The influence of secondary slip on the tensile characteristics of ordered crystals was determined by using specimens oriented for multiple glide. It is demonstrated that the work hardening rate increases with the occurrence of secondary slip. The strain-aging phenomena shown previously in poly crystalline Ni3Fe was found to occur also in single crystals. The nature of the observed effects in ordered Ni3Fe is interpreted in terms of the antiphase boundary tube mechanism.